Título : | Influência do tipo de cimento resinoso no comportamento mecânico de uma resina nano cerâmica |
metadata.dc.creator: | Meneghetti, Daniel Eduardo |
metadata.dc.contributor.advisor1: | Borba, Márcia |
metadata.dc.description.resumo: | A resina nano cerâmica para CAD/CAM tem 80% de carga inorgânica em suacomposição, possui similaridade à dentina humana, e pelos elementos poliméricoscontidos, tem reduzida friabilidade. O objetivo deste estudo é avaliar a influência do tipo de cimento resinoso no comportamento mecânico de uma resina nano cerâmica(Lava Ultimate, LVU). Foram avaliados dois cimentos resinosos duais: autoadesivo(RelyX U200, 3M) e convencional (Rely X Ultimate, 3M), em dois testes, resistência flexural e carga compressiva. Para o teste de resistência flexural, foram confeccionados discos de LVU (n=10), que receberam uma camada de cimento e foram armazenados em água destilada, em uma câmara a 37ºC durante seis meses. Depois desse tempo foi realizado o teste de flexão biaxial de acordo com o método piston-on-three-balls , e os dados avaliados com o teste Mann-Whitney (α=0,05). Para o teste de carga de fratura,foram confeccionadas lâminas de LVU, que foram cimentadas sobre um material análogo à dentina (NEMA G10) utilizando os dois tipos de cimentos resinosos (n=10).Antes do teste de carga compressiva, os dois grupos foram submetidos a um envelhecimento através de ciclagem mecânica (50 N a 2 Hz, 500.000 ciclos). Os dados foram analisados com Teste t (α=0,05). Não houve diferença estatística entre os grupos para resistência flexural. O tipo de cimento não afetou a carga de fratura e o modo de falha dos corpos-de-prova avaliados no teste de carga compressiva. Conclui-se que o tipo de cimento resinoso não tem influência no comportamento mecânico da resina nano cerâmica. |
Resumen : | The nanoceramic resin for CAD/CAM has 80% of inorganic load in its composition, it has similarity to human dentin, and due to the polymeric elements contained, it has reduced friability. The aim of this study is to evaluate the influence of the type of resin cement on the mechanical behavior of a nanoceramic resin (Lava Ultimate, LVU). Two dual resin cements were evaluated: self-adhesive (RelyX U200, 3M) and conventional (Rely X Ultimate, 3M), in two tests, flexural strength and compressive load. For the flexural resistance test, LVU discs (n=10) were made, which received a layer of cement and were stored in distilled water, in a chamber at 37ºC for six months. After that time, the biaxial flexion test was performed according to the piston-on-three-balls method, and the data evaluated with the Mann-Whitney test (α=0.05). For the fracture load test, LVU sheets were made, which were cemented on a material similar to dentin (NEMA G10) using both types of resin cements (n=10). Before the compressive load test, both groups were subjected to mechanical aging (50 N at 2 Hz, 500,000 cycles). Data were analyzed with t test (α=0.05). There was no statistical difference between groups for flexural strength. The type of cement did not affect the fracture load and the failure mode of the specimens evaluated in the compressive load test. It is concluded that the type of resin cement has no influence on the mechanical behavior of the nanoceramic resin. |
Palabras clave : | Odontologia Cimentação Cimentos dentários Materiais dentários |
metadata.dc.language: | por |
metadata.dc.publisher.country: | Brasil |
Editorial : | Universidade de Passo Fundo |
metadata.dc.publisher.initials: | UPF |
metadata.dc.publisher.department: | Faculdade de Odontologia - FO |
Citación : | MENEGHETTI, Daniel Eduardo. Influência do tipo de cimento resinoso no comportamento mecânico de uma resina nano cerâmica. 2019. 26 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2019. |
metadata.dc.rights: | Acesso Aberto |
URI : | http://repositorio.upf.br/handle/riupf/2032 |
Fecha de publicación : | 29-may-2019 |
Aparece en las colecciones: | FO - Curso de Odontologia - Trabalhos de Conclusão de Curso de Graduação |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
PF2019DanielEduardoMeneghetti.pdf | Trabalho de conclusão de curso de Daniel Eduardo Meneghetti | 1,6 MB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.